Experimental Investigation on the Effect of Nano Carbon Tube on Concrete Strength

Document Type: Original Article

Authors

Department of Civil Engineering, Islamic Azad University, Ahvaz Branch, Khouzestan, Iran.

10.22034/jcema.2020.215337.1013

Abstract

This work presents in evaluation in regard to the addition of CNTs dispersion in water ultrasound before it incorporation to concrete mass. The dispersion of carbon Nano tubes have been achieved by use of surfactants and other chemical compounds along with vigorous agitation by signification. The various researches have reported varied results experimenting with different amounts of CNTs and different dispersion techniques leading to a conclusion that 0.03 to 0.5% additions of CNTs to cement enhance the properties greatly. Nano particles are filled the porosity of concrete, therefore reduced permeability and increased the concrete strength and its sustainability. In this research, Nano carbon tube for enhancing the physical properties was used. For the experimental work in this research 5 control specimens 50 x 50 x 50 mm and 5 samples containing 0.03% Nano carbon as percentage of sand and cement, specimens were made based on ASTM C349. With considering the results obtained from experiment, the 0.03% CNT multi wall added to the mortar the strength increased by 39%, this can be attributed to the dispersion of CNT in concrete and protecting concrete from progressive cracks. In the other words, treated CNT in composite concrete matrix, provided more surface connection due to high specific areas resulted transferring more forces, so they provided better connection, therefore preventing matrix surrounding from any micro-structures cracks of the samples were also improved properties greatly.

Keywords


[1] Marcondes CG, Medeiros MH, Marques Filho J, Helene P. Nanotubos de carbono en concreto de cemento Portland. Influencia de la dispersión en las propiedades mecánicas y en la absorción de agua. Revista ALCONPAT. 2015 Aug;5(2):97-114.[View at Google Scholar] ; [View at Publisher].
[2] Jha SA, Jethwani S, Sangtiani D. Carbon Nanotube Cement Composites. International Journal of Civil Engineering and Technology (IJCIET). 2016;7(5). [View at Google Scholar] ; [View at Publisher].
[3] Manzur T, Yazdani N, Emon M, Bashar A. Potential of carbon nanotube reinforced cement composites as concrete repair material. Journal of Nanomaterials. 2016;2016. [View at Google Scholar] ; [View at Publisher].
[4] Al Araj R, Tamimi AK. Sustainability of Carbon Nanotube-Reinforced Concrete. International Journal of Structural and Construction Engineering. 2017 May 1;11(7):881-7. [View at Google Scholar] ; [View at Publisher].
[5] Tyson BM, Abu Al-Rub RK, Yazdanbakhsh A, Grasley Z. Carbon nanotubes and carbon nanofibers for enhancing the mechanical properties of nanocomposite cementitious materials. Journal of Materials in Civil Engineering. 2011 Jul 1;23(7):1028-35. [View at Google Scholar] ; [View at Publisher].
[6] Altoubat S, Yazdanbakhsh A, Rieder KA. Shear behavior of macro-synthetic fiber-reinforced concrete beams without stirrups. ACI Materials Journal. 2009 Jul 1;106(4):381. [View at Google Scholar] ; [View at Publisher].
[7] Fischer G, Li VC. Effect of fiber reinforcement on the response of structural members. Engineering Fracture Mechanics. 2007 Jan 1;74(1-2):258-72. [View at Google Scholar] ; [View at Publisher].
[8] Li VC, Maalej M. Toughening in cement based composites. Part II: Fiber reinforced cementitious composites. Cement and Concrete Composites. 1996 Jan 1;18(4):239-49. [View at Google Scholar] ; [View at Publisher].
[9] Ostertag CP, Yi C, Vondran G. Tensile strength enhancement in interground fiber cement composites. Cement and Concrete Composites. 2001 Aug 1;23(4-5):419-25. [View at Google Scholar] ; [View at Publisher].
[10] Savastano Jr H, Warden PG, Coutts RS. Microstructure and mechanical properties of waste fibre–cement composites. Cement and Concrete Composites. 2005 May 1;27(5):583-92. [View at Google Scholar] ; [View at Publisher].
[11] Wang C, Li KZ, Li HJ, Jiao GS, Lu J, Hou DS. Effect of carbon fiber dispersion on the mechanical properties of carbon fiber-reinforced cement-based composites. Materials Science and Engineering: A. 2008 Jul 25;487(1-2):52-7. [View at Google Scholar] ; [View at Publisher].
[12] Coleman JN, Khan U, Blau WJ, Gun’ko YK. Small but strong: a review of the mechanical properties of carbon nanotube–polymer composites. Carbon. 2006 Aug 1;44(9):1624-52. [View at Google Scholar] ; [View at Publisher].
[13] Marrs B, Andrews R, Pienkowski D. Multiwall carbon nanotubes enhance the fatigue performance of physiologically maintained methyl methacrylate–styrene copolymer. Carbon. 2007 Sep 1;45(10):2098-104. [View at Google Scholar] ; [View at Publisher].
[14] Wang, J. G., Fang, Z. P., Gu, A. J., Xu, L. H., and Liu, F. 2006. “Effect of amino-functionalization of multi-walled carbon nanotubes on the dispersion with epoxy resin matrix.” J. Appl. Polym. Sci., 100(1), 97–104. [View at Google Scholar] ; [View at Publisher].
[15] Zhou Z, Lai C, Zhang L, Qian Y, Hou H, Reneker DH, Fong H. Development of carbon nanofibers from aligned electrospun polyacrylonitrile nanofiber bundles and characterization of their microstructural, electrical, and mechanical properties. Polymer. 2009 Jun 19;50(13):2999-3006. [View at Google Scholar] ; [View at Publisher].
[16] Yu MF, Lourie O, Dyer MJ, Moloni K, Kelly TF, Ruoff RS. Strength and breaking mechanism of multiwalled carbon nanotubes under tensile load. Science. 2000 Jan 28;287(5453):637-40. [View at Google Scholar] ; [View at Publisher].
[17] Chen W, Auad ML, Williams RJ, Nutt SR. Improving the dispersion and flexural strength of multiwalled carbon nanotubes–stiff epoxy composites through β-hydroxyester surface functionalization coupled with the anionic homopolymerization of the epoxy matrix. European Polymer Journal. 2006 Oct 1;42(10):2765-72. [View at Google Scholar] ; [View at Publisher].
[18] Grunlan JC, Liu L, Regev O. Weak polyelectrolyte control of carbon nanotube dispersion in water. Journal of colloid and interface science. 2008 Jan 1;317(1):346-9. [View at Google Scholar] ; [View at Publisher].
[19] Xie XL, Mai YW, Zhou XP. Dispersion and alignment of carbon nanotubes in polymer matrix: a review. Materials science and engineering: R: Reports. 2005 May 19;49(4):89-112. [View at Google Scholar] ; [View at Publisher].
[20] Cwirzen A, Habermehl-Cwirzen K, Penttala V. Surface decoration of carbon nanotubes and mechanical properties of cement/carbon nanotube composites. Advances in cement research. 2008 Apr;20(2):65-73. [View at Google Scholar] ; [View at Publisher].
[21] Siddique R, Mehta A. Effect of carbon nanotubes on properties of cement mortars. Construction and Building Materials. 2014 Jan 15;50:116-29. [View at Google Scholar] ; [View at Publisher].
[22] ASTM C642-97, Standard Test Method for Density, Absorption, and Voids in hardened concrete.  [View at Publisher].
[23] ASTM C348, Standard Test Method for Flow of Hydraulic Cement Mortar, Annual Book of Standards 2017. [View at Publisher].
[24] ASTM C. Standard test method for electrical indication of concrete’s ability to resist chloride ion penetration. C1202–18. 2012. [View at Google Scholar] ; [View at Publisher].
[25] Hasehmpour H, Mohammadi Atashgah K, Karbalaei Rezaei M. An investigation into the role of nano-silica in improving strength of lightweight concrete. European Online Journal of Natural and Social Sciences. 2014 Nov 12;3(4):pp-1058. [View at Google Scholar] ; [View at Publisher].